ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened
Equivalent material: ASTM Grade F48, DIN 1.4439, DIN G-X3CrNiMoN17-13-5, DIN X2CrNiMoN17-13-5, AFNOR Z3CND18-14-05Az, UNE F.3544, AISI 317LMN, SAE 317LMN, JIS SUS317J1, EN X2CrNiMoN17-13-5, EN 1.4439, ASTM 317LMN, UNS S31726
ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened general
Property |
Temperature |
Value |
Comment |
Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened chemical
Property |
Value |
Carbon |
Carbon of 0.3 % |
Manganese |
Manganese of 1.6 % |
Phosphorus |
Phosphorus of 0.03 % |
Silicon |
Silicon of 0.15 - 0.35 % |
Sulfur |
Sulfur of 0.025 % |
ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened magnetic
Property |
Temperature |
Value |
Comment |
Curie temperature |
20.0 °C |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened electrical
Property |
Temperature |
Value |
Comment |
Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A694 Grade F48 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened mechanical
Property |
Temperature |
Value |
Comment |
Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
Elongation A50 |
20.0 °C |
Elongation A50 of 20 % |
- |
Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
Tensile strength |
20.0 °C |
Tensile strength of 425 MPa |
- |
Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 330 MPa |
- |