ASTM A513 Grade 1010 Sink-Drawn
Equivalent material: UNS G10100, DIN 1.1121, DIN Ck10, DIN C10E, AFNOR C10RR, AFNOR XC 10, AFNOR C10E, BS 040A10, BS En2A, BS En2B, BS 040A04, BS 040A12, BS C10E, BS 045M10, BS En32A, UNI C10, SS 1264, AISI 1010, SAE 1010, JIS S10C, JIS S09CK, JIS S12C, JIS SWRCH10K, JIS SWCH10K, EN C10E, EN HX300LAD, EN 1.1121, ISO C10, ISO C10E, ISO S10C, GOST 10, GOST 08, GB 10, GB/T 10, GB/T U20102, ASTM M1010, ASTM Grade 1010
ASTM A513 Grade 1010 Sink-Drawn general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A513 Grade 1010 Sink-Drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A513 Grade 1010 Sink-Drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 - 0.13 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.035 % |
ASTM A513 Grade 1010 Sink-Drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A513 Grade 1010 Sink-Drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A513 Grade 1010 Sink-Drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 8 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 65 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 345 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 275 MPa |
- |