ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes
Equivalent material: DIN 1.0032, DIN St 34-2, AISI 1010, SAE 1010, JIS STKM13B, JIS 13B, JIS E185-0, EN 1.0032, UNS G10100, IS Fe310, IS 10C4, IS C10
ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 - 0.15 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.045 % |
ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A512 Grade MT1010 Stress Relief Annealed Round Tubes mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 15 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 70 - 90 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 434 - 689 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 400 MPa |
- |
Our stringent quality control measures ensure consistent and reliable steel products.
-- Our promise