ASTM A240 Grade 329 Heat-Treated
Equivalent material: DIN 1.4460, DIN X4CrNiMoN27-5-2, DIN X8CrNiMo27-5, DIN X3CrNiMoN27-5-2, AFNOR Z5CND27-05Az, BS X3CrNiMoN27-5-2, AISI 329, SAE 329, JIS SUS329J1TP, JIS SUS329J1TPY, JIS SUS329J1TB, JIS SCS11, EN X3CrNiMoN27-5-2, EN 1.4460, ISO X3CrNiMoN27-5-2, ISO 4460-312-00-I, ISO DM34F, ISO 55, ASTM Grade F50, UNS S32900, JIS SUS329J1, ASTM S32900
ASTM A240 Grade 329 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Duplex Stainless Steel |
ASTM A240 Grade 329 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
Typical for Duplex Stainless Steel |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 502 J/(kg·K) |
Typical for Duplex Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 - 30 W/(m·K) |
Typical for Duplex Stainless Steel |
ASTM A240 Grade 329 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 23 - 28 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 1 - 2 % |
| Nickel |
Nickel of 2 - 5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.75 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A240 Grade 329 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
Typical for Duplex Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 15 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 269 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 28 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 620 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 485 MPa |
- |