AISI 317 Hot Finished
Equivalent material: DIN 1.4449, AFNOR Z6CND17-12-04, SAE 317, JIS SUS317, JIS SUS317TP, JIS SUS317TB, JIS SUS317TPY, JIS SUSF317, EN X3CrNiMo18-12-3, EN 1.4449, UNS S31700, ASTM TP317, ASTM 317, ASTM F317, ASTM S31700, ASTM MT317
AISI 317 Hot Finished general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 317 Hot Finished thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| Melting point |
- |
Melting point of 1380 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 480 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
AISI 317 Hot Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.08 % |
| Chromium |
Chromium of 18 - 20 % |
| Iron |
Iron of 58 - 68 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 3 - 4 % |
| Nickel |
Nickel of 11 - 15 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 0.75 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 317 Hot Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 317 Hot Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 56 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 590 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 250 MPa |
- |