EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT)
EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT) introduction
The corrosion resistant material X3CrNiMo18-12-3, material number 1.4449 is predominantly used for pressure vessel construction.
Equivalent material: GB 06Cr19Ni13Mo3, GB S31708, JIS SUSF317, KS STSF317, ASTM A965 Grade F317, UNS S31700, ISO X5CrNiMo17-3, ASTM Grade F317, ASTM F317, DIN 1.4449, AFNOR Z6CND17-12-04, AISI 317, SAE 317, JIS SUS317, JIS SUS317TP, JIS SUS317TB, JIS SUS317TPY, EN 1.4449
EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 g/cm³ |
EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.035 % |
| Chromium |
Chromium of 17 - 18.2 % |
| Copper |
Copper of 1 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.25 - 2.75 % |
| Nickel |
Nickel of 11.5 - 12.5 % |
| Nitrogen |
Nitrogen of 0.08 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 Ω·m |
EN 10222-5 Grade X3CrNiMo18-12-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 40 - 45 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 520 - 720 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 220 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 255 MPa |
- |