JIS G4305 Grade SUS317 solution treated
Equivalent material: GB/T 0Cr19Ni13Mo3, GB/T 0Cr18Ni12Mo3Ti, GB 0Cr19Ni13Mo3, AS 317, BS 317S16, UNI X5CrNiMo1815, EN X3CrNiMo18-12-3, SIS 2353-22, SIS 2353-23, SIS 2353-24, SIS 2353-25, SIS 2353-26, SIS 2353-27, SIS 2353-28, SIS 2353-29, SIS 2366, ASME 317, ASTM TP317, ASTM 317, ASTM CR317, ASTM WP317, ASTM 19Cr 13Ni 3.5Mo, ASTM F317, ASTM MT317, MIL 317, JIS SUSY317, AISI 317, SAE 317, UNS S31700, ASTM S31700, DIN 1.4449, AFNOR Z6CND17-12-04, JIS SUS317TP, JIS SUS317TB, JIS SUS317TPY, JIS SUSF317, EN 1.4449
JIS G4305 Grade SUS317 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS317 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS317 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS317 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |