JIS G4305 Grade SUS317L solution treated
Equivalent material: GB/T 00Cr19Ni13Mo3, GB/T 0Cr18Ni16Mo5, GB 00Cr19Ni13Mo3, GB 0Cr18Ni16Mo5, GB 00Cr17Ni14Mo3, AS 317L, DIN X2CrNiMo18164, EN X2CrNiMo18-15-4, NF Z2CND19-15, NF Z2CND19-14, NF Z3CND19-15-04, NF Z2CND19-15-04, BS 317S12, UNI X2CrNiMo1816, UNI X2CrNiMo1815, ÖNORM X2CrNiMo18164KW, UNE X2CrNiMo18164, SIS 2367, ASME 317L, ASTM TP317L, ASTM CR317L, ASTM WP317L, ASTM 317L, ASTM 19Cr 13Ni 3.5Mo, ASTM F317L, JIS SUS317LTP, AISI 317L, SAE 317L, UNS S31703, DIN 1.4438, DIN X2CrNiMo18-16-4, DIN X2CrNiMo18-15-4, AFNOR Z3CND19-15-04, SS 2367, UNE F.3539, AISI TP 317L, SAE TP 317L, JIS SUS317LTPY, JIS SUS317LTB, JIS SUS317LFB, JIS SUSF317L, EN 1.4438, UNS S31700
JIS G4305 Grade SUS317L solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS317L solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS317L solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS317L solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 480 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |