AISI 1038 Hot Rolled
Equivalent material: DIN 1.1150, DIN C38D2, AFNOR C38D2, BS C38D2, SAE 1038, EN C38D2, EN 1.1150, ISO C38D2, GB C38D2, GB/T C38D2, ASTM 1038, UNS G10380, DIN 1.1181, DIN Ck35, DIN C35E, AFNOR C35E, AFNOR XC38H2, AFNOR C35RR, AFNOR XC35, AFNOR 9160C021, AFNOR 9160/C23, AFNOR XC38, AFNOR XC32, AFNOR XC38H1, BS En5, BS 080M30, BS C35E, BS 080M36, BS CFS6, AISI 1035, AISI 1038H, AISI C1034, SAE 1035, SAE 1038H, SAE C1034, JIS S35C, JIS S35CM, JIS CS35, EN C35E, EN 1.1181, ISO C35E, ISO C35E4, ISO CE35E4, ISO CS35, ISO S38C, GOST 35, GB 35, GB U20352, GB/T ZG35, GB/T C22750, GB/T ZG270-500, GB/T 35, GB/T U20352, UNS H10380, UNS G10350
AISI 1038 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1038 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
AISI 1038 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.35 - 0.42 % |
| Iron |
Iron of 98.6 - 99.05 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1038 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1038 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 21 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 600 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 330 MPa |
- |