AISI 1012 Hot Rolled
Equivalent material: DIN 1.0214, DIN QSt 36-3, DIN C10C, AFNOR C10C, BS C10C, SAE 1012, JIS SWCH10, JIS SWRCH10A, JIS SWRCH10R, JIS SWCH10A, JIS SWCH10R, EN C10C, EN 1.0214, GB/T ML10Al, GB/T U40108, UNS G10120, DIN 1.0311, DIN C12D, AFNOR C12D, BS C12D, JIS SWRM12, JIS SWRM12K, EN C12D, EN 1.0311, ISO C12D, DIN 1.1124, DIN C12D2, AFNOR C12D2, BS C12D2, EN C12D2, EN 1.1124, ISO C12D2, ASTM M1012, ASTM 1012, ASTM Grade 1012, DIN 1.1130, DIN C12E, EN 1.1130, IS C7, IS C10
AISI 1012 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 1012 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
AISI 1012 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.1 - 0.15 % |
| Iron |
Iron of 99.16 - 99.6 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1012 Hot Rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
AISI 1012 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1012 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 350 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 200 MPa |
- |