AISI 1010 Cold Drawn

Equivalent material: DIN 1.0032, DIN St 34-2, SAE 1010, JIS STKM13B, JIS 13B, JIS E185-0, EN 1.0032, ASTM MT1010, UNS G10100, IS Fe310, IS 10C4, IS C10, DIN 1.0301, DIN C10, AFNOR C10, BS C10, BS 045M10, JIS S09SK, JIS S10C, EN C10, EN HX340LAD, EN 1.0301, ISO CE10, GOST 10, GB/T 10, GB/T U20102, DIN 1.0310, DIN D 10-2, DIN C10D, AFNOR C10D, BS C10D, JIS SWRM10, JIS SWRM10K, EN C10D, EN 1.0310, ISO C10D, DIN 1.1114, DIN C10D2, AFNOR C10D2, BS C10D2, EN C10D2, EN 1.1114, ISO C10D2, ASTM M1010, ASTM Grade 1010, DIN 1.1121, DIN Ck10, DIN C10E, AFNOR C10RR, AFNOR XC 10, AFNOR C10E, BS 040A10, BS En2A, BS En2B, BS 040A04, BS 040A12, BS C10E, BS En32A, UNI C10, SS 1264, JIS S09CK, JIS S12C, JIS SWRCH10K, JIS SWCH10K, EN C10E, EN HX300LAD, EN 1.1121, ISO C10, ISO C10E, ISO S10C, GOST 08, GB 10, ASTM 1010, DIN 1.1207, DIN C10R, AFNOR C10R, BS C10R, EN C10R, EN 1.1207, ISO C10R

AISI 1010 Cold Drawn general

Property Temperature Value
Density 23.0 °C Density of 7.9 g/cm³

AISI 1010 Cold Drawn thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 450 J/(kg·K) -
Thermal conductivity 23.0 °C Thermal conductivity of 25 - 93 W/(m·K) Typical for Low Carbon Steel

AISI 1010 Cold Drawn chemical

Property Value
Carbon Carbon of 0.08 - 0.13 %
Iron Iron of 99.18 - 99.62 %
Manganese Manganese of 0.3 - 0.6 %
Phosphorus Phosphorus of 0 - 0.04 %
Sulfur Sulfur of 0 - 0.05 %

AISI 1010 Cold Drawn magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

AISI 1010 Cold Drawn electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

AISI 1010 Cold Drawn mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 210 GPa -
Elongation 23.0 °C Elongation of 22 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 23.0 °C Tensile strength of 400 MPa -
Yield strength 23.0 °C Yield strength of 330 MPa -