AISI 1010 Hot Rolled
Equivalent material: DIN 1.0032, DIN St 34-2, SAE 1010, JIS STKM13B, JIS 13B, JIS E185-0, EN 1.0032, ASTM MT1010, UNS G10100, IS Fe310, IS 10C4, IS C10, DIN 1.0301, DIN C10, AFNOR C10, BS C10, BS 045M10, JIS S09SK, JIS S10C, EN C10, EN HX340LAD, EN 1.0301, ISO CE10, GOST 10, GB/T 10, GB/T U20102, DIN 1.0310, DIN D 10-2, DIN C10D, AFNOR C10D, BS C10D, JIS SWRM10, JIS SWRM10K, EN C10D, EN 1.0310, ISO C10D, DIN 1.1114, DIN C10D2, AFNOR C10D2, BS C10D2, EN C10D2, EN 1.1114, ISO C10D2, ASTM M1010, ASTM Grade 1010, DIN 1.1121, DIN Ck10, DIN C10E, AFNOR C10RR, AFNOR XC 10, AFNOR C10E, BS 040A10, BS En2A, BS En2B, BS 040A04, BS 040A12, BS C10E, BS En32A, UNI C10, SS 1264, JIS S09CK, JIS S12C, JIS SWRCH10K, JIS SWCH10K, EN C10E, EN HX300LAD, EN 1.1121, ISO C10, ISO C10E, ISO S10C, GOST 08, GB 10, ASTM 1010, DIN 1.1207, DIN C10R, AFNOR C10R, BS C10R, EN C10R, EN 1.1207, ISO C10R
AISI 1010 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 1010 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
AISI 1010 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 - 0.13 % |
| Iron |
Iron of 99.18 - 99.62 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1010 Hot Rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
AISI 1010 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1010 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 350 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 190 MPa |
- |
Our skilled craftsmen ensure meticulous attention to detail for superior steel products.