AISI 1006 Hot Rolled
Equivalent material: DIN 1.0313, DIN D 6-2, DIN D 8-2, DIN C7D, AFNOR C7D, BS C7D, SAE 1006, JIS SWRM6, JIS SWRM6K, EN C7D, EN 1.0313, ISO C7D, GOST SWRM6, ASTM 1006, UNS G10060, DIN 1.1111, DIN C5D2, AFNOR C5D2, BS C5D2, EN C5D2, EN 1.1111, ISO C5D2, ASTM Grade 1006, DIN 1.0335, DIN DD13, AFNOR DD13, BS DD13, JIS SPHE, JIS SEHE, JIS SPHD, EN 1.0335, ISO CR23, ISO HR4, GOST 08kp
AISI 1006 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 1006 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
AISI 1006 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.08 % |
| Iron |
Iron of 99.43 - 99.75 % |
| Manganese |
Manganese of 0.25 - 0.4 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1006 Hot Rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
AISI 1006 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1006 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 32 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 350 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 180 MPa |
- |