UNS S30815 Annealed
Equivalent material: DIN 1.4835, DIN X10CrNiSiN21-11, DIN X9CrNiSiNCe21-11-2, AISI 253MA, SAE 253MA, EN X9CrNiSiNCe21-11-2, EN 1.4835, ASTM F45, ASTM S30815, AISI S30815, SAE S30815
UNS S30815 Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.7 g/cm³ |
UNS S30815 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
UNS S30815 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 - 0.12 % |
| Cerium |
Cerium of 0.03 - 0.08 % |
| Chromium |
Chromium of 20 - 22 % |
| Iron |
Iron of 62 - 68.4 % |
| Manganese |
Manganese of 0 - 1 % |
| Nickel |
Nickel of 10 - 12 % |
| Nitrogen |
Nitrogen of 0.12 - 0.2 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 1.4 - 2.5 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
UNS S30815 Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
UNS S30815 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 46 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 690 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 360 MPa |
- |