UNS S20910 Hot Rolled
Equivalent material: ASTM TPXM-19, ASTM XM-19, ASTM S20910, ASTM Grade FXM-19, ASTM FXM-19, ASTM Grade 8R, AISI XM-19, SAE XM-19, ASTM Grade B8R, ASTM Grade B8RA, ASTM Grade 8RA
UNS S20910 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
UNS S20910 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 480 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 W/(m·K) |
- |
UNS S20910 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.06 % |
| Chromium |
Chromium of 20.5 - 23.5 % |
| Iron |
Iron of 52.1 - 62.1 % |
| Manganese |
Manganese of 4 - 6 % |
| Molybdenum |
Molybdenum of 1.5 - 3 % |
| Nickel |
Nickel of 11.5 - 13.5 % |
| Niobium |
Niobium of 0.1 - 0.3 % |
| Nitrogen |
Nitrogen of 0.2 - 0.4 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Silicon |
Silicon of 0 - 0.75 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
| Vanadium |
Vanadium of 0.1 - 0.3 % |
UNS S20910 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
UNS S20910 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 23 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 480 MPa |
- |
Experience the strength, resilience, and versatility of our premium steel products.