ASTM A193 Grade B8RA Class 1C, Carbide solution treated in the finished condition
Equivalent material: ASTM Grade B8R, ASTM Grade B8RA, ASTM Grade 8R, ASTM Grade 8RA, UNS S20910
ASTM A193 Grade B8RA Class 1C, Carbide solution treated in the finished condition general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A193 Grade B8RA Class 1C, Carbide solution treated in the finished condition thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A193 Grade B8RA Class 1C, Carbide solution treated in the finished condition chemical
| Property |
Value |
| Carbon |
Carbon of 0.06 % |
| Chromium |
Chromium of 20.5 - 23.5 % |
| Manganese |
Manganese of 4 - 6 % |
| Molybdenum |
Molybdenum of 1.5 - 3 % |
| Nickel |
Nickel of 11.5 - 13.5 % |
| Niobium |
Niobium of 0.1 - 0.3 % |
| Nitrogen |
Nitrogen of 0.2 - 0.4 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
| Vanadium |
Vanadium of 0.1 - 0.3 % |
ASTM A193 Grade B8RA Class 1C, Carbide solution treated in the finished condition electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A193 Grade B8RA Class 1C, Carbide solution treated in the finished condition mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 35 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 271 [-] |
- |
| Hardness, Rockwell C |
20.0 °C |
Hardness, Rockwell C of 28 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 55 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 690 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 380 MPa |
- |