ASTM A276 Grade S20910 Annealed
ASTM A276 Grade S20910 Annealed introduction
NITRONIC® 50 is manganese alloyed austenitic stainless steel with improved corrosion resistance compared to 316L and 317L due to increased chromium content plus about twice the yield strength of the same at room temperature. Unlike many austenitic alloys, NITRONIC® 50 does not become magnetic when cold formed. NITRONIC® 50 Stainless has very good mechanical properties at both elevated and sub-zero temperatures.
Equivalent material: ASTM Grade XM-19, ASTM TPXM-19, ASTM XM-19, ASTM S20910, ASTM Grade FXM-19, ASTM FXM-19, ASTM Grade 8R, AISI XM-19, SAE XM-19, ASTM Grade B8R, ASTM Grade B8RA, ASTM Grade 8RA
ASTM A276 Grade S20910 Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
ASTM A276 Grade S20910 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy, V-notch |
23.0 °C |
Charpy impact energy, V-notch of 230 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 35 - 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 201 - 293 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 655 - 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 440 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 345 - 420 MPa |
- |
ASTM A276 Grade S20910 Annealed chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0 - 0.06 % |
- |
| Chromium |
Chromium of 20.5 - 23.5 % |
- |
| Iron |
Iron of 52.1 - 62.1 % |
Balance |
| Manganese |
Manganese of 4 - 6 % |
- |
| Molybdenum |
Molybdenum of 1.5 - 3 % |
- |
| Nickel |
Nickel of 11.5 - 13.5 % |
- |
| Niobium |
Niobium of 0.1 - 0.3 % |
- |
| Nitrogen |
Nitrogen of 0.2 - 0.4 % |
- |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
- |
| Silicon |
Silicon of 0 - 1 % |
- |
| Sulfur |
Sulfur of 0 - 0.03 % |
- |
| Vanadium |
Vanadium of 0.1 - 0.3 % |
- |
ASTM A276 Grade S20910 Annealed magnetic
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A276 Grade S20910 Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 480 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 W/(m·K) |
- |
ASTM A276 Grade S20910 Annealed mechanical
| Property |
Value |
| Diameter |
Diameter of 25.4 - 140 mm |