UGICHROM® 4307
UGICHROM® 4307 introduction
UGICHROM® is the result of combining the high efficiency of micro-fissuring chromium plating with the technology of the most advanced stainless steel bars. The UGICHROM® product range is recommended for hydraulic and pneumatic mechanisms.
General properties - choice for performance:
Low friction coefficient.
High resistance to wear.
Increased corrosion resistance.
Micro-fissuring chromium plating guarantees excellent performance under extreme conditions of service.
Improved machinability (up to +20% of productivity).
High mechanical properties.
Accurate geometrical and dimensional properties..
Equivalent material: EN 1.4307, EN X2CrNi18-9, AISI 304L, DIN 1.4307, DIN X2CrNi18-9
UGICHROM® 4307 general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGICHROM® 4307 thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.000016 1/K |
20 to 100°C |
| - |
Coefficient of thermal expansion of 0.0000165 1/K |
20 to 200°C |
| - |
Coefficient of thermal expansion of 0.000017 1/K |
20 to 300°C |
| - |
Coefficient of thermal expansion of 0.000018 1/K |
20 to 400°C, 20 to 500°C |
| Specific heat capacity |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
Thermal conductivity of 15 W/(m·K) |
- |
UGICHROM® 4307 chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.03 |
max. |
| Chromium |
Chromium of 18.0 - 19.0 % |
- |
| Copper |
Copper of 0.75 |
max. |
| Manganese |
Manganese of 0.5 - 1.5 % |
- |
| Molybdenum |
Molybdenum of 0.5 |
max. |
| Nickel |
Nickel of 8.0 - 9.5 % |
- |
| Nitrogen |
Nitrogen of 0.1 |
max. |
| Phosphorus |
Phosphorus of 0.04 |
max. |
| Silicon |
Silicon of 0.75 |
max. |
| Sulfur |
Sulfur of 0.02 - 0.03 % |
- |
UGICHROM® 4307 electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.3e-07 Ω·m |
UGICHROM® 4307 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20 °C |
Elastic modulus of 200 GPa |
- |
| - |
100 °C |
Elastic modulus of 194 GPa |
- |
| - |
200 °C |
Elastic modulus of 186 GPa |
- |
| - |
300 °C |
Elastic modulus of 179 GPa |
- |
| - |
400 °C |
Elastic modulus of 172 GPa |
- |
| - |
500 °C |
Elastic modulus of 165 GPa |
- |
| Tensile strength |
- |
Tensile strength of 450 MPa |
min. |
UGICHROM® 4307 application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
| Other |
CHARACTERISTICS |
Standard product |
Special product |
| Diameter tolerance |
ISO f7 |
On request |
| Bar length dia. 12 to 19 mm |
2900 mm +200/-0 |
On request |
| Bar length dia. 20 to 125 mm |
6000 mm +/- 500 mm |
On request |
| Roundness |
<1/2 f7 ISO |
- |
| Straightness (to EN 10278) |
<0.5 mm/ml |
Up to 0.2 mm for dia. >30 mm |
| Roughness |
Ra < 0.2 µm |
Up to Ra <0.08 µm |
| Chromium structure |
Microcracked |
- |
| Sizes |
Dia. 12 to 125 mm |
On request |
| Thickness of the chromium dia. 12 to 19.5 mm |
18 µm +/-3 |
Max. 50 µm |
| Thickness of the chromium dia. 20 to 115 mm |
25 µm +/-5 |
Max. 100 µm |