EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT)
EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT) introduction
The austenitic steel X2CrNi18-9 is available in solution annealed condition in the form of cold rolled strip, warm rolled strip and warm rolled sheet. The material is resistant to intercrystalline corrosion also in welded condition.
Equivalent material: UNS S30403, ASTM 304L, ASME 304L, GB 022Cr19Ni10, GB S30403, ISO X2CrNi18-10, JIS SUS304LTB, KS STS304LTB, ASTM A213Type304L, ASME SA-213Type304L, AISI 304L, AISI Type304L, DIN 1.4307, DIN G-X2CrNiN18-9, AFNOR Z3CN19-09, BS 304S11, SS 2352, SAE 304L, JIS SUS304L, EN 1.4307, GOST 03Ch18N11, GB 00Cr19Ni10, ASTM TP304L, IS X02Cr18Ni11
EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 17.5 - 19.5 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8 - 10 % |
| Nitrogen |
Nitrogen of 0.1 - 0.11 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.3E-7 Ω·m |
EN 10216-5 Grade X2CrNi18-9 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 35 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 460 - 680 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 460 - 680 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 180 MPa |
- |
| - |
50.0 °C |
Yield strength Rp0.2 of 165 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 145 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 130 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 118 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 108 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 100 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 94 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 89 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 85 MPa |
- |
| - |
500.0 °C |
Yield strength Rp0.2 of 81 MPa |
- |
| - |
550.0 °C |
Yield strength Rp0.2 of 80 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 180 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 215 MPa |
- |
| - |
50.0 °C |
Yield strength Rp1.0 of 200 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 180 MPa |
- |
| - |
150.0 °C |
Yield strength Rp1.0 of 160 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 145 MPa |
- |
| - |
250.0 °C |
Yield strength Rp1.0 of 135 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 127 MPa |
- |
| - |
350.0 °C |
Yield strength Rp1.0 of 121 MPa |
- |
| - |
400.0 °C |
Yield strength Rp1.0 of 116 MPa |
- |
| - |
450.0 °C |
Yield strength Rp1.0 of 112 MPa |
- |
| - |
500.0 °C |
Yield strength Rp1.0 of 109 MPa |
- |
| - |
550.0 °C |
Yield strength Rp1.0 of 108 MPa |
- |
| Yield strength Rp1.0, transverse |
20.0 °C |
Yield strength Rp1.0, transverse of 215 MPa |
- |
Our diverse range of steel products caters to endless applications across industries.