SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q)
SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q) introduction
G-X 2 CrNiMoN 18 10, for cast parts with increased resistance against intercristalline corrosion. no treatment after welding necessary
Equivalent material: ISO C57, ISO C61LC, DIN 1.4404, DIN X2CrNiMo18-10, DIN X2CrNiMo17-12-2, DIN G-X2CrNiMoN18-14, DIN GX2CrNiMoN18-14, DIN X2CrNiMoN17-12-2, DIN X2CrNiMo17-13-2, AFNOR Z2CND17-12, BS 316S12, UNI X2CrNiMo1712, SS 2343, SS 2348, SS 2553, AISI 316L, SAE 316L, JIS SUS316L, JIS SCS16, EN X2CrNiMo17-12-2, EN 1.4404, GOST 03Ch17N13M2, GB 022Cr17Ni12Mo2, ASTM 316L, UNS S31603, IS X02Cr17Ni12Mo2
SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.85E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 17 - 20 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 9 - 13 % |
| Nitrogen |
Nitrogen of 0.1 - 0.2 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1.5 % |
| Sulfur |
Sulfur of 0.02 % |
SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
SEW 410 Grade G-X2CrNiMoN18-10 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 - 640 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 140 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 110 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 92 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 85 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 80 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 230 MPa |
- |