SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched
SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched introduction
The fully austenitic material G-X 2 CrNiMoN 18 14, with the material number 1.3952 according to SEW 395-87 (invalidly replaced by GX2CrNiMoN18-14, material number 1.3960 according to SEW 395-98), possesses a defined low value of the relative magnetic permeability of 1.01 maximum (for castings with a wall thickness of up to 50 mm). It is applied for construction components which an interference or shielding of a magnetic field must not occur at.
(SEW: steel-iron material specification)
Equivalent material: DIN 1.4404, DIN X2CrNiMo18-10, DIN X2CrNiMo17-12-2, DIN GX2CrNiMoN18-14, DIN X2CrNiMoN17-12-2, DIN X2CrNiMo17-13-2, DIN G-X2CrNiMoN18-10, AFNOR Z2CND17-12, BS 316S12, UNI X2CrNiMo1712, SS 2343, SS 2348, SS 2553, AISI 316L, SAE 316L, JIS SUS316L, JIS SCS16, EN X2CrNiMo17-12-2, EN 1.4404, GOST 03Ch17N13M2, GB 022Cr17Ni12Mo2, ASTM 316L, UNS S31603, IS X02Cr17Ni12Mo2
SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 13 - 15 % |
| Nitrogen |
Nitrogen of 0.15 - 0.25 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.02 % |
SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 Ω·m |
SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 490 - 690 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 240 MPa |
- |