Sandvik 8R61 is an austenitic chromium-nickel steel alloyed with molybdenum for high-temperature applications.

Datasheet URL:
Sandvik 8R61

Datasheet updated 2019-09-02 09:20 (supersedes all previous editions)

Equivalent material: AISI 316H, EN 1.4918, DIN 1.4918, EN X6CrNiMo17-13-2, DIN X6CrNiMo17-13

Sandvik 8R61 general

Property Temperature Value Comment
Density 23.0 °C Density of 7.9 g/cm³ -
Recycled Content - Recycled Content of 82.1 % Average recycled content

Sandvik 8R61 chemical

Property Value Comment
Carbon Carbon of 0.06 % max.
Chromium Chromium of 17.5 % -
Iron -
Manganese Manganese of 1.4 % -
Molybdenum Molybdenum of 2.2 % -
Nickel Nickel of 12 % -
Phosphorus Phosphorus of 0.04 % max.
Silicon Silicon of 0.5 % -
Sulfur Sulfur of 0.015 % max.

Sandvik 8R61 electrical

Property - -
Welding

Sandvik 8R61 mechanical

Property Temperature Value Comment
Charpy impact energy -196.0 °C Charpy impact energy of 60 J EN 13445-2 (UFPV-2) and EN 10216-5
Creep strength 10^4 cycles 550.0 °C Creep strength 10^4 cycles of 250 MPa ISO values, at 10000h
- 560.0 °C Creep strength 10^4 cycles of 235 MPa ISO values, at 10000h
- 570.0 °C Creep strength 10^4 cycles of 220 MPa ISO values, at 10000h
- 580.0 °C Creep strength 10^4 cycles of 205 MPa ISO values, at 10000h
- 590.0 °C Creep strength 10^4 cycles of 190 MPa ISO values, at 10000h
- 600.0 °C Creep strength 10^4 cycles of 175 MPa ISO values, at 10000h
- 610.0 °C Creep strength 10^4 cycles of 160 MPa ISO values, at 10000h
- 620.0 °C Creep strength 10^4 cycles of 147 MPa ISO values, at 10000h
- 630.0 °C Creep strength 10^4 cycles of 135 MPa ISO values, at 10000h
- 640.0 °C Creep strength 10^4 cycles of 123 MPa ISO values, at 10000h
- 650.0 °C Creep strength 10^4 cycles of 111 MPa ISO values, at 10000h
- 660.0 °C Creep strength 10^4 cycles of 100 MPa ISO values, at 10000h
- 670.0 °C Creep strength 10^4 cycles of 91 MPa ISO values, at 10000h
- 680.0 °C Creep strength 10^4 cycles of 82 MPa ISO values, at 10000h
- 690.0 °C Creep strength 10^4 cycles of 73 MPa ISO values, at 10000h
- 700.0 °C Creep strength 10^4 cycles of 65 MPa ISO values, at 10000h
Creep strength 10^5 cycles 550.0 °C Creep strength 10^5 cycles of 175 MPa ISO values, at 100000h
- 560.0 °C Creep strength 10^5 cycles of 164 MPa ISO values, at 100000h
- 570.0 °C Creep strength 10^5 cycles of 153 MPa ISO values, at 100000h
- 580.0 °C Creep strength 10^5 cycles of 142 MPa ISO values, at 100000h
- 590.0 °C Creep strength 10^5 cycles of 131 MPa ISO values, at 100000h
- 600.0 °C Creep strength 10^5 cycles of 120 MPa ISO values, at 100000h
- 610.0 °C Creep strength 10^5 cycles of 109 MPa ISO values, at 100000h
- 620.0 °C Creep strength 10^5 cycles of 98 MPa ISO values, at 100000h
- 630.0 °C Creep strength 10^5 cycles of 88 MPa ISO values, at 100000h
- 640.0 °C Creep strength 10^5 cycles of 78 MPa ISO values, at 100000h
- 650.0 °C Creep strength 10^5 cycles of 69 MPa ISO values, at 100000h
- 660.0 °C Creep strength 10^5 cycles of 60 MPa ISO values, at 100000h
- 670.0 °C Creep strength 10^5 cycles of 52 MPa ISO values, at 100000h
- 680.0 °C Creep strength 10^5 cycles of 46 MPa ISO values, at 100000h
- 690.0 °C Creep strength 10^5 cycles of 40 MPa ISO values, at 100000h
- 700.0 °C Creep strength 10^5 cycles of 34 MPa ISO values, at 100000h
Elongation 23.0 °C Elongation of 35 % min.
Tensile strength 23.0 °C Tensile strength of 490 - 690 MPa -
Yield strength Rp0.2 20.0 °C Yield strength Rp0.2 of 205 MPa min.
- 50.0 °C Yield strength Rp0.2 of 184 MPa min.
- 100.0 °C Yield strength Rp0.2 of 177 MPa min.
- 150.0 °C Yield strength Rp0.2 of 162 MPa min.
- 200.0 °C Yield strength Rp0.2 of 147 MPa min.
- 250.0 °C Yield strength Rp0.2 of 137 MPa min.
- 300.0 °C Yield strength Rp0.2 of 127 MPa min.
- 350.0 °C Yield strength Rp0.2 of 122 MPa min.
- 400.0 °C Yield strength Rp0.2 of 118 MPa min.
- 450.0 °C Yield strength Rp0.2 of 113 MPa min.
- 500.0 °C Yield strength Rp0.2 of 108 MPa min.
- 550.0 °C Yield strength Rp0.2 of 103 MPa min.