SAE J403 Grade 1070
Equivalent material: DIN 1.0615, DIN D 70-2, DIN C70D, AFNOR C70D, BS C70D, AISI 1070, EN C70D, EN 1.0615, ISO C70D, GOST 70, GOST 3K-7, GB 70, GB U20702, GB/T 70, GB/T U20702, GB/T C70D, GB/T U53702, GB/T U59702, ASTM Grade 1070M, UNS G10700, DIN 1.0617, DIN D 73-2, DIN C72D, AFNOR C72D, BS C72D, JIS SWRH72, JIS SWRH72A, EN C72D, EN 1.0617, ISO C72D, GB C72D, GB U53722, GB/T C72D, GB/T U53722, GB/T U59722, DIN 1.1231, DIN Ck67, DIN C67S, AFNOR C68RR, AFNOR XC68, AFNOR C67S, BS C67S, BS 70CS, BS 70HS, UNI C70, JIS S70CM, JIS S70C-CSP, JIS SWRH72B, JIS S70C, EN C67S, EN 1.1231, ISO CS65, GOST 65G, GOST 65GA, GOST 65, GB 65, GB U20652, GB/T 65, GB/T U20652, ASTM 1070, IS C70, DIN 1.1244, DIN 70Mn4, AFNOR 70Mn4, BS 70Mn4, JIS 70Mn4, EN 1.1244, ISO 70Mn4, ISO B42, GB/T 70Mn, GB/T U21702, DIN 1.9613, DIN SAE 1070, EN 1.9613, DIN 1.0603, DIN C67, AFNOR C68, EN 1.0603, ISO CS70, DIN 1.1248, DIN Ck75, DIN C75S, AFNOR C75S, AFNOR C75RR, AFNOR XC75, BS 060A78, BS C75S, BS CS70, BS 80, AISI 1075, AISI 1078, AISI 1074, SAE 1075, SAE 1078, SAE 1074, JIS S75CM, JIS SWRH77B, EN C75S, EN 1.1248, ISO CS75, GOST 75, GOST 75A, GB/T 75, GB/T U20752, ASTM Grade 1074, UNS G10750, UNS G10780, UNS G10740
SAE J403 Grade 1070 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
SAE J403 Grade 1070 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
SAE J403 Grade 1070 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.65 - 0.75 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.035 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1070 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1070 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |