AISI 1070 Hot Rolled
Equivalent material: DIN 1.0615, DIN D 70-2, DIN C70D, AFNOR C70D, BS C70D, SAE 1070, EN C70D, EN 1.0615, ISO C70D, GOST 70, GOST 3K-7, GB 70, GB U20702, GB/T 70, GB/T U20702, GB/T C70D, GB/T U53702, GB/T U59702, ASTM Grade 1070M, UNS G10700, DIN 1.0617, DIN D 73-2, DIN C72D, AFNOR C72D, BS C72D, JIS SWRH72, JIS SWRH72A, EN C72D, EN 1.0617, ISO C72D, GB C72D, GB U53722, GB/T C72D, GB/T U53722, GB/T U59722, DIN 1.1231, DIN Ck67, DIN C67S, AFNOR C68RR, AFNOR XC68, AFNOR C67S, BS C67S, BS 70CS, BS 70HS, UNI C70, JIS S70CM, JIS S70C-CSP, JIS SWRH72B, JIS S70C, EN C67S, EN 1.1231, ISO CS65, GOST 65G, GOST 65GA, GOST 65, GB 65, GB U20652, GB/T 65, GB/T U20652, ASTM 1070, IS C70, DIN 1.1244, DIN 70Mn4, AFNOR 70Mn4, BS 70Mn4, JIS 70Mn4, EN 1.1244, ISO 70Mn4, ISO B42, GB/T 70Mn, GB/T U21702, DIN 1.9613, DIN SAE 1070, EN 1.9613, DIN 1.0603, DIN C67, AFNOR C68, EN 1.0603, ISO CS70, DIN 1.1248, DIN Ck75, DIN C75S, AFNOR C75S, AFNOR C75RR, AFNOR XC75, BS 060A78, BS C75S, BS CS70, BS 80, AISI 1075, AISI 1078, AISI 1074, SAE 1075, SAE 1078, SAE 1074, JIS S75CM, JIS SWRH77B, EN C75S, EN 1.1248, ISO CS75, GOST 75, GOST 75A, GB/T 75, GB/T U20752, ASTM Grade 1074, UNS G10750, UNS G10780, UNS G10740
AISI 1070 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1070 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
AISI 1070 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.65 - 0.75 % |
| Iron |
Iron of 98.3 - 98.8 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1070 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1070 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 13 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 760 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 410 MPa |
- |