AISI 1078 Hot Rolled
Equivalent material: DIN 1.0622, DIN D 80-2, DIN C80D, AFNOR C80D, BS C80D, SAE 1078, JIS SWRH82B, EN C80D, EN 1.0622, ISO C80D, GOST 80, GB 80, GB U20802, GB/T C80D, GB/T U53802, GB/T 80, GB/T U20802, GB/T U59803, UNS G10780, DIN 1.0626, DIN D 83-2, DIN C82D, AFNOR C82D, BS C82D, JIS SWRH82, JIS SWRH82A, EN C82D, EN 1.0626, ISO C82D, GB C82D, GB U59823, GB/T C82D, GB/T U53822, GB/T U59823, DIN 1.1255, DIN D80-3, DIN C80D2, AFNOR C80D2, BS C80D2, JIS SWRS80, EN C80D2, EN 1.1255, ISO C80D2, GB/T C80D2, DIN 1.1262, DIN D83-3, DIN C82D2, AFNOR C82D2, BS C82D2, JIS SUP3, EN C82D2, EN 1.1262, ISO C82D2, GB/T C82D2, GB/T U53827, GB/T U53828, GB/T YL82A, GB/T YL82B, DIN 1.1248, DIN Ck75, DIN C75S, AFNOR C75S, AFNOR C75RR, AFNOR XC75, BS 70CS, BS 70HS, BS 060A78, BS C75S, BS CS70, BS 80, AISI 1070, AISI 1075, AISI 1074, SAE 1070, SAE 1075, SAE 1074, JIS S75CM, JIS SWRH77B, EN C75S, EN 1.1248, ISO CS75, GOST 75, GOST 75A, GB/T 75, GB/T U20752, ASTM Grade 1074, ASTM Grade 1070M, UNS G10700, UNS G10750, UNS G10740
AISI 1078 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1078 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
AISI 1078 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.72 - 0.85 % |
| Iron |
Iron of 98.5 - 99 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1078 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1078 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 14 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 440 MPa |
- |