SAE J403 Grade 1060
Equivalent material: DIN 1.0601, DIN C60, AFNOR CC55, AFNOR C60, BS 080A62, BS 60CS, BS 60HS, BS En9, BS 070M55, BS C60, BS 060A62, UNI C60, AISI 1060, JIS S60C, JIS S58C, JIS SWRH62B, JIS S65C, EN C60, EN 1.0601, ISO C60, ISO CS60, GOST 2, GOST 60, GOST 60G, GB/T 60, GB/T CRB970, GB/T U20602, ASTM 1060, UNS G10600, DIN 1.0609, DIN D 58-2, DIN C58D, AFNOR C58D, BS C58D, JIS SWRH57, JIS SWRH57A, JIS CS55, EN C58D, EN 1.0609, ISO C58D, GB/T C58D, GB/T U53582, DIN 1.0610, DIN D 60-2, DIN C60D, AFNOR C60D, BS C60D, JIS CS60, EN C60D, EN 1.0610, ISO C60D, GB/T C60D, GB/T U53602, DIN 1.1223, DIN Cm 60, DIN Cm60, DIN C60R, AFNOR C60R, BS C60R, EN C60R, EN 1.1223, ISO C60R, ISO C60M2
SAE J403 Grade 1060 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
SAE J403 Grade 1060 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
SAE J403 Grade 1060 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.55 - 0.65 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.035 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1060 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1060 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |