EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered
EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered introduction
Steel C 60 is suitable for high ductility parts and parts of increased wear resistance requirements in vehicle manufacturing, engine and machine engineering
surface hardenable (e.g. transmission parts, shafts, axles). Additional application in tooling. Lowest application temp. -25 °C.
Equivalent material: NBN C60-1, BS 070M60, GOST 60, ISO C60, UNI C60, PN 60, ASTM 1060, DIN 1.0601, AFNOR CC55, AFNOR C60, BS 080A62, BS 60CS, BS 60HS, BS En9, BS 070M55, BS C60, BS 060A62, AISI 1060, SAE 1060, JIS S60C, JIS S58C, JIS SWRH62B, JIS S65C, EN C60, EN 1.0601, ISO CS60, GOST 2, GOST 60G, GB/T 60, GB/T CRB970, GB/T U20602, UNS G10600
EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 41.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.4 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 43.2 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.4 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.7 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.5E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.95E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.65E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.53E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.74E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
EN 10277-5 Grade C60 cold drawn or turned and quenched and tempered mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 208.26 - 212 GPa |
| - |
100.0 °C |
Elastic modulus of 203.78 - 207 GPa |
| - |
200.0 °C |
Elastic modulus of 198.06 - 199 GPa |
| - |
300.0 °C |
Elastic modulus of 190.8 - 192 GPa |
| - |
400.0 °C |
Elastic modulus of 182.61 - 184 GPa |
| - |
500.0 °C |
Elastic modulus of 173.04 - 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation |
20.0 °C |
Elongation of 11 - 14 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.27 [-] |
| - |
100.0 °C |
Poisson's ratio of 0.27 [-] |
| - |
200.0 °C |
Poisson's ratio of 0.28 [-] |
| - |
300.0 °C |
Poisson's ratio of 0.28 [-] |
| - |
400.0 °C |
Poisson's ratio of 0.28 [-] |
| - |
500.0 °C |
Poisson's ratio of 0.28 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 25 - 35 % |
| Shear modulus |
20.0 °C |
Shear modulus of 82.04 GPa |
| - |
100.0 °C |
Shear modulus of 80.18 GPa |
| - |
200.0 °C |
Shear modulus of 77.56 GPa |
| - |
300.0 °C |
Shear modulus of 74.62 GPa |
| - |
400.0 °C |
Shear modulus of 71.22 GPa |
| - |
500.0 °C |
Shear modulus of 67.36 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 750 - 1000 MPa |
| Yield strength |
20.0 °C |
Yield strength of 450 - 580 MPa |