JIS G5121 Grade SCS1
Equivalent material: GB 1Cr12, GB 1Cr13, GOST 12Х13, GOST 12H13, GOST 12H13-Sh, GOST 15H13L, AS H3A, AS 410, DIN X10Cr13, NF Z12C13, NF Z12CN13M, NF Z10C13, BS 410S21, BS 420C29, BS 410S21-690, BS 410S21-720, BS 410S21-760, BS 410S21-750, BS 410S21-770, BS 410C21, UNI GX12Cr13, UNI X12Cr13, UNI X10Cr13, UNI X12Cr13KG, UNI X12Cr13KW, EN X12Cr13, UNE X10Cr13, SIS 2302, AMS 5351, ASTM CPCA15, ASTM CA15, ASTM CA15-A, ASTM CA15M-A, ASTM CA15-B, ASTM CA15-C, ASTM CA15-D, MIL Class 1, MIL 410, JIS SUS410, GB/T 1Cr12, DIN 1.4008, DIN G-X8CrNi13, EN GX7CrNiMo12-1, EN 1.4008, UNS J91150
JIS G5121 Grade SCS1 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G5121 Grade SCS1 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G5121 Grade SCS1 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G5121 Grade SCS1 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 16 - 18 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 163 - 241 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 - 40 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 540 - 620 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 345 - 450 MPa |
- |