JIS G4802 Grade S70C quenched and tempered
Equivalent material: DIN 1.1231, DIN Ck67, DIN C67S, AFNOR C68RR, AFNOR XC68, AFNOR C67S, BS C67S, BS 70CS, BS 70HS, UNI C70, AISI 1070, SAE 1070, JIS S70CM, JIS S70C-CSP, JIS SWRH72B, EN C67S, EN 1.1231, ISO CS65, GOST 65G, GOST 65GA, GOST 65, GB 65, GB U20652, GB/T 65, GB/T U20652, ASTM 1070, ASTM Grade 1070M, UNS G10700, IS C70, DIN 1.0603, DIN C67, AFNOR C68, EN 1.0603, ISO CS70, GOST 70
JIS G4802 Grade S70C quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
JIS G4802 Grade S70C quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
JIS G4802 Grade S70C quenched and tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4802 Grade S70C quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 350 - 550 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |