JIS G4305 Grade SUS430LX annealed
Equivalent material: NF X8CT17, NF X8CR17, ASME 439, ASTM TP439, ASTM 439, AISI 439, AISI S4, AISI S43035, SAE 439, DIN 1.4509, AISI 441, SAE 441, EN X2CrTiNb18, EN 1.4509, ASTM S43940, UNS S43940, DIN 1.4511, DIN X6CrNb17, AFNOR Z4CNb17, EN X3CrNb17, EN X6CrNb17, EN 1.4511, DIN 1.4520, DIN X1CrTi15, EN X2CrTi17, EN X1CrTi15, EN 1.4520, UNS S43035, DIN 1.4510, DIN X3CrTi17, DIN GX40CrSi29, DIN X6CrTi17, JIS SUS430LXTP, JIS SUS430LXTB, JIS SUSXM8TB, EN X3CrTi17, EN 1.4510, UNS S43036
JIS G4305 Grade SUS430LX annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS430LX annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS430LX annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS430LX annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 88 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 360 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |