JIS G4304 Grade SUS420J1 annealed
Equivalent material: GB 2Cr13, GOST 20Х13, GOST 20H13, GOST 20H13-Sh, AS 420, DIN X20Cr13, NF Z20C13, NF X40Cr14, BS 420S45, BS 420S37, IS 20Cr13, IS 30Cr13, IS 40Cr13, UNI X20Cr13, UNI X41Cr13KU, UNE X20Cr13, UNE F.310.J, SIS 2303-02, SIS 2303-03, SIS 2303-04, SIS 2303-08, SIS 2303, SIS 2314, AMS 5506, AMS 5621, AMS 7207, ASTM 420, ASTM 422, MIL 420, AISI 420, GB/T 2Cr13, GB/T 2Cr13-Q, EN X20Cr13, DIN 1.4021, DIN X30Cr13, AFNOR Z20C13, BS 420S29, SS 2303, SAE 420, JIS SUS 420J1, JIS SUS420J1FB, JIS SUS420J1TKA, EN 1.4021, ISO 20Cr13, GOST 20Ch13, UNS S42000
JIS G4304 Grade SUS420J1 annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4304 Grade SUS420J1 annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4304 Grade SUS420J1 annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4304 Grade SUS420J1 annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 223 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 97 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 234 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 225 MPa |
- |