EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800)
EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800) introduction
Material X39Cr13 is comparable to X 38 Cr 13 acc. to DIN 17440 : 1985-07. The material is used for the production of cutting tools (knife blades, scissors, cutting surgical instruments), ball bearing balls, abrasion resistant components for controlling and pump parts, springs, piston rods, screws. Application in hardened condition with a honed and polished surface, in this case resistant to water and steam. Corrosion resistance is insufficient in annealed or high tempered condition.
Application temperature up to 200 deg (for the comparable DIN-material)
Equivalent material: GB 4Cr13, CSN 17024, AFNOR Z40C14, GOST 40Ch13, GB S42040, ISO X39Cr13, UNI X40Cr14, STAS 40Cr130, SS 2304, UNE F.3404, UNE X40Cr13, MSZ KO13, ISO 4031-420-00-I, ISO MP13P, GOST 40Х13, ASTM A959UNSS42000, AISI 420, AISI 420C, AISI 420HC, DIN X38Cr13, DIN 1.4031, BS 420S45, SAE 420, EN 1.4031, UNS S42000
EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 - 7.71 g/cm³ |
EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.02E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.09E-5 - 1.1E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.13E-5 - 1.15E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.16E-5 - 1.2E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.22E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 200 °C |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 439 - 460 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 474 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 498 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 538 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 564 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 598 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 24.6 - 30 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 24.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 25 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 25.2 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 25.5 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 25.8 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 26 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 7.3 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 6.4 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 5.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.8 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.1 mm²/s |
- |
EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800) chemical
| Property |
Value |
| Carbon |
Carbon of 0.36 - 0.42 % |
| Chromium |
Chromium of 12.5 - 14.5 % |
| Manganese |
Manganese of 1 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 5.5E-7 - 5.87E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 6.55E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 7.38E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 8.19E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 8.96E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 9.7E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.04E-6 Ω·m |
EN 10088-1 Grade X39Cr13 quenched and tempered (+QT800) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 215 - 222 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 212 - 216 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 205 - 209 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 200 - 201 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 190 - 192 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 183 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 174 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 7 - 10 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 800 - 1100 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 800 - 1100 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 650 - 700 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 650 - 700 MPa |
- |
Get the best value for your money with our top-grade steel at competitive prices.
-- Our promise