JIS G4304 Grade SUS405 annealed
Equivalent material: GB 0Cr13Al, AS 405, DIN X6CrAl13, NF Z6CA13, NF Z8CA12, BS 713, BS 405S17, UNI X6CrAl13, EN X6CrAl13, UNE X6CrAl13, ASME 405, ASTM TP405, ASTM 405, ASTM MT405, MIL 405, AISI 405, SAE 405, GB/T 0Cr13Al, DIN 1.4724, DIN X10CrAl13, AFNOR Z10C13, BS 403S17, UNI X10CrA112, UNE F.311, EN X10CrAlSi13, EN 1.4724, DIN 1.4002, AFNOR Z8CA12, AFNOR X6CrAl13, BS X6CrAl13, AISI S40500, SAE S40500, JIS SUS405TB, JIS SUS405TP, EN 1.4002, ISO 66, ISO 4002-405-00-I, ISO FP13H, ISO X6CrAl13, GB/T 0Cr13Al, GB/T 06Cr13Al, GB/T S11348, UNS S40500
JIS G4304 Grade SUS405 annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS405 annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS405 annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS405 annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 88 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 410 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |