ASTM A473 Grade 405 Annealed
Equivalent material: DIN 1.4002, DIN X6CrAl13, AFNOR Z8CA12, AFNOR X6CrAl13, BS 405S17, BS X6CrAl13, UNI X6CrAl13, AISI 405, AISI S40500, SAE 405, SAE S40500, JIS SUS405, JIS SUS405TB, JIS SUS405TP, EN X6CrAl13, EN 1.4002, ISO 66, ISO 4002-405-00-I, ISO FP13H, ISO X6CrAl13, GB/T 0Cr13Al, GB/T 06Cr13Al, GB/T S11348, ASTM MT405, ASTM TP405, UNS S40500
ASTM A473 Grade 405 Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
ASTM A473 Grade 405 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
ASTM A473 Grade 405 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 11.5 - 14.5 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A473 Grade 405 Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
ASTM A473 Grade 405 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 207 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 415 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
Our steel seamlessly integrates into your projects, ensuring flawless and impressive outcomes.