JIS G4303 Grade SUS304LN solution treated
Equivalent material: GB/T 00Cr18Ni10N, GB 00Cr18Ni10N, GB 00Cr18Ni10, DIN X2CrNiN1810, EN X2CrNiN18-10, NF Z2CN18-10AZ, NF Z3CN18-07Az, NF Z3CN18-10Az, BS 304S61, UNI X2CrNiN1811, ÖNORM X2CrNiN1810KKW, UNE X2CrNiN1810, SIS 2371, ASTM TP304LN, ASTM 304LN, ASTM B8LN, ASTM B8LNA, ASTM CR304LN, ASTM WP304LN, ASTM 18Cr 8Ni Mod. with Ni, ASTM F304LN, ASTM 8LN, ASTM 8LNA, AISI 304LN, SAE 304LN, ASTM S30453, UNS S30453, ASTM Grade 8LN, DIN 1.4311, DIN X2CrNiN18-10, AFNOR Z3CN18-10, BS 304S62, UNI X2CrNiN1810, SS 2371, JIS SUSF304LN, EN 1.4311
JIS G4303 Grade SUS304LN solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS304LN solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS304LN solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS304LN solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 217 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 220 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 550 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 245 MPa |
- |