EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT)
EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT) introduction
The austenitic CrNi-Stahl X2CrNiN18-10, comparable to X 2 CrNiN 18 10 acc. to DIN 17440 : 1985-07, shows a higher yield point due to alloying of nitrogen which is adhered even at higher temperatures. Using in pressure vessel construction and in light weight construction. Improved corrosion resistance by N-content. The material is resistant to intercrystalline corrosion also in sensitized condition. Suitability for chemical apparatus engineering as a result of resistance to nitrous acid and other oxidizing media. The steel is well cold formable and usable for mirror finishing.
Equivalent material: GB 022Cr19Ni10N, GB S30453, ISO X2CrNiN18-10, JIS SUSF304LN, KS STSF304LN, ASTM A473Type304LN, SAE 304LN, SAE Type304LN, UNS S30453, DIN 1.4311, DIN X2CrNiN18-10, AFNOR Z3CN18-10, BS 304S62, UNI X2CrNiN1810, SS 2371, AISI 304LN, JIS SUS304LN, EN 1.4311, GB 00Cr18Ni10N
EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.9 - 7.93 g/cm³ |
EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.88E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.91E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 472 - 500 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.3 - 15 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 15.8 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 17.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 19 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 20.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.9 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 23.3 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.6 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 26 W/(m·K) | - |
| - | 900.0 °C | Thermal conductivity of 27.4 W/(m·K) | - |
| - | 1000.0 °C | Thermal conductivity of 28.8 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4.2 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.3 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.6 mm²/s | - |
| - | 900.0 °C | Thermal diffusivity of 5.9 mm²/s | - |
| - | 1000.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 17 - 19.5 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 8.5 - 11.5 % |
| Nitrogen | Nitrogen of 0.12 - 0.22 % |
| Phosphorus | Phosphorus of 0.05 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.03 % |
EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.1E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 7.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 8.49E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.14E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 9.71E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.02E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.14E-6 Ω·m |
| - | 900.0 °C | Electrical resistivity of 1.17E-6 Ω·m |
| - | 1000.0 °C | Electrical resistivity of 1.19E-6 Ω·m |
EN 10250-4 Grade X2CrNiN18-10 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa | - |
| - | 20.0 °C | Elastic modulus of 196 - 200 GPa | - |
| - | 100.0 °C | Elastic modulus of 190 - 194 GPa | - |
| - | 200.0 °C | Elastic modulus of 182 - 186 GPa | - |
| - | 300.0 °C | Elastic modulus of 174 - 179 GPa | - |
| - | 400.0 °C | Elastic modulus of 166 - 172 GPa | - |
| - | 500.0 °C | Elastic modulus of 158 - 165 GPa | - |
| - | 600.0 °C | Elastic modulus of 150 GPa | - |
| - | 700.0 °C | Elastic modulus of 142 GPa | - |
| - | 800.0 °C | Elastic modulus of 134 GPa | - |
| - | 900.0 °C | Elastic modulus of 127 GPa | - |
| - | 1000.0 °C | Elastic modulus of 120 GPa | - |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 30 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 550 - 760 MPa | - |
| Yield strength Rp0.2 | 100.0 °C | Yield strength Rp0.2 of 205 MPa | - |
| - | 150.0 °C | Yield strength Rp0.2 of 175 MPa | - |
| - | 200.0 °C | Yield strength Rp0.2 of 157 MPa | - |
| - | 250.0 °C | Yield strength Rp0.2 of 145 MPa | - |
| - | 300.0 °C | Yield strength Rp0.2 of 136 MPa | - |
| - | 350.0 °C | Yield strength Rp0.2 of 130 MPa | - |
| - | 400.0 °C | Yield strength Rp0.2 of 125 MPa | - |
| - | 450.0 °C | Yield strength Rp0.2 of 121 MPa | - |
| - | 500.0 °C | Yield strength Rp0.2 of 119 MPa | - |
| - | 550.0 °C | Yield strength Rp0.2 of 118 MPa | - |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 270 MPa | - |
| Yield strength Rp1.0 | 100.0 °C | Yield strength Rp1.0 of 240 MPa | - |
| - | 150.0 °C | Yield strength Rp1.0 of 210 MPa | - |
| - | 200.0 °C | Yield strength Rp1.0 of 187 MPa | - |
| - | 250.0 °C | Yield strength Rp1.0 of 175 MPa | - |
| - | 300.0 °C | Yield strength Rp1.0 of 167 MPa | - |
| - | 350.0 °C | Yield strength Rp1.0 of 161 MPa | - |
| - | 400.0 °C | Yield strength Rp1.0 of 156 MPa | - |
| - | 450.0 °C | Yield strength Rp1.0 of 152 MPa | - |
| - | 500.0 °C | Yield strength Rp1.0 of 149 MPa | - |
| - | 550.0 °C | Yield strength Rp1.0 of 147 MPa | - |
| Yield strength Rp1.0, transverse | 20.0 °C | Yield strength Rp1.0, transverse of 305 MPa | - |
Our quality control measures guarantee the highest standards of steel.
-- Our promise
Similar or equivalent steel materials
- EN 10088-1 Grade X2CrNiN18-10 solution annealed (+AT)
- EN 10028-7 Grade X2CrNiN18-10 solution annealed (+AT)
- DIN 17440 Grade X2CrNiN18-10 solution heat-treated and quenched
- DIN 17440 Grade X2CrNiN18-10 quenched (+Q)
- EN 10272 Grade X2CrNiN18-10 solution annealed (+AT)
- EN 10216-5 Grade X2CrNiN18-10 solution annealed (+AT)
- DIN 1654-5 Grade X2CrNiN18-10 quenched (+Q)
- EN 10217-7 Grade X2CrNiN18-10 solution annealed (+AT)
- EN 10222-5 Grade X2CrNiN18-10 solution annealed (+AT)
- DIN 1654-5 Grade X2CrNiN18-10 cold drawn and quenched