JIS G4303 Grade SUS202 solution treated
Equivalent material: GB 1Cr18Mn8Ni5N, GOST 12Х17Г9АН4, GOST 12H17G9AN4, NF Z8CNM19-8, ASTM TP202, ASTM 202, AISI 202, SAE 202, GB/T 1Cr18Mn8Ni5N, EN X2CrMnNiN17-7-5, DIN 1.4371, DIN X2CrMnNiN17-7-5, AFNOR X2CrMnNiN17-7-5, BS X2CrMnNiN17-7-5, AISI S20103, AISI 201LN, AISI 201L, AISI S20153, SAE S20103, SAE 201LN, SAE 201L, SAE S20153, EN 1.4371, ASTM TP201LN, UNS S20153, UNS S20103, DIN 1.4373, BS 284S16, EN X12CrMnNiN18-9-5, EN 1.4373, GOST 12X17 9AH4, UNS S20200
JIS G4303 Grade SUS202 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS202 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS202 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS202 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 207 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 218 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 275 MPa |
- |