EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700)
EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700) introduction
The austenitic material X2CrMnNiN17-7-5 is used in solution annealed condition in the form of cold rolled strip, warm rolled strip and warm rolled sheet. It is resistant to intercrystalline corrosion also in sensitized condition.
Equivalent material: GB 1Cr18Mn8Ni5N, BS 202S16, GB S35450, JIS SUS202, KS STS202, ISO 4371-201-53-I, ISO AP29B, ASTM A240UNSS20153, ASTM A480UNSS20153, ASTM A666UNSS20153, ASTM A959UNSS20153, UNS S20153, AISI Type201LN, DIN 1.4371, DIN X2CrMnNiN17-7-5, AFNOR X2CrMnNiN17-7-5, BS X2CrMnNiN17-7-5, AISI S20103, AISI 201LN, AISI 201L, AISI S20153, SAE S20103, SAE 201LN, SAE 201L, SAE S20153, EN 1.4371, ASTM TP201LN, UNS S20103
EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.85E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 16 - 17.5 % |
| Copper |
Copper of 1 % |
| Manganese |
Manganese of 6 - 8 % |
| Nickel |
Nickel of 3.5 - 5.5 % |
| Nitrogen |
Nitrogen of 0.15 - 0.25 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7E-7 Ω·m |
EN 10088-1 Grade X2CrMnNiN17-7-5 strain-hardened (+C700) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 700 - 850 MPa |
- |