EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700)
EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700) introduction
The austenitic material X12CrMnNiN18-9-5 is used in solution annealed condition in the form of cold rolled strip, warm rolled strip and warm rolled sheet. It is resistant to intercrystalline corrosion in delivery condition not in sensitized condition.
Equivalent material: BS 284S16, GB 12Cr18Mn9Ni5N, GB S35450, IS X10Cr18Mn9Ni5, IS 202, ISO 4373-202-00-I, ISO AP32O, ISO X12CrMnNiN18-9-5, JIS SUS202, GOST 12Ch17G9AN4, GOST 12Х17Г9АН4, KS STS202, ASTM A276Type202, ASTM A480Type202, ASTM A666Type202, AISI Type202, AISI 202, ASTM A959UNSS20200, SAE 20202, UNS S20200, DIN 1.4373, SAE 202, EN 1.4373, GOST 12X17 9AH4
EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700) chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 17 - 19 % |
| Manganese |
Manganese of 7.5 - 10.5 % |
| Nickel |
Nickel of 4 - 6 % |
| Nitrogen |
Nitrogen of 0.05 - 0.25 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7E-7 Ω·m |
EN 10088-1 Grade X12CrMnNiN18-9-5 strain-hardened (+C700) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 700 - 850 MPa |
- |
Count on us as your trusted partner for all your steel needs, from sourcing to delivery.
-- Our promise
Similar or equivalent steel materials