JIS G3459 Grade SUS430TP

JIS G3459 Grade SUS430TP

Equivalent material: DIN 1.4016, DIN X6Cr17, DIN X8Cr17, DIN X3CrTi17, AFNOR Z8C17, BS 430S15, UNI X8Cr17, SS 2320, UNE F.3113, AISI 430, SAE 430, JIS SUS430, JIS SUS430TB, JIS SUS430TKA, JIS SUS430TKC, JIS SUSY430, EN X6Cr17, EN 1.4016, ISO X6Cr17, ISO F1, GOST 12Ch17, GB 1Cr17, ASTM S43000, UNS S43000

JIS G3459 Grade SUS430TP general

Property Temperature Value Comment
Density 23.0 °C Density of 7.6 - 7.8 g/cm³ Typical for Ferritic Stainless Steel

JIS G3459 Grade SUS430TP thermal

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 220 GPa Typical for Ferritic Stainless Steel
Elongation A5 23.0 °C Elongation A5 of 5 - 20 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Ferritic Stainless Steel
Shear modulus 23.0 °C Shear modulus of 77 GPa Typical for Ferritic Stainless Steel
Tensile strength 23.0 °C Tensile strength of 410 MPa -
Yield strength Rp0.2 23.0 °C Yield strength Rp0.2 of 245 MPa -

JIS G3459 Grade SUS430TP magnetic

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 6E-7 - 7.5E-7 Ω·m Typical for Ferritic Stainless Steel

JIS G3459 Grade SUS430TP electrical

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K Typical for Ferritic Stainless Steel
Melting point - Melting point of 1425 - 1530 °C Typical for Ferritic Stainless Steel
Specific heat capacity 23.0 °C Specific heat capacity of 420 - 586 J/(kg·K) Typical for Ferritic Stainless Steel
Thermal conductivity 23.0 °C Thermal conductivity of 11 - 22 W/(m·K) Typical for Ferritic Stainless Steel

JIS G3459 Grade SUS430TP mechanical

Property Value
Wall thickness Wall thickness of 1 - 8 mm