DIN 5512-3 Grade X6Cr17 soft annealed (+A)
DIN 5512-3 Grade X6Cr17 soft annealed (+A) introduction
The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-3 up to 12 mm thickness.
The corresponding properties of EN 10088 shall be taken.
Application examples: door and window profiles, fittings, holders, racks, radiator covers
Remark: Only suitable for resistance welding. Resistant to intercrystalline corrosion in the delivery condition.
Equivalent material: GB 10Cr17, GB S11710, IS X07Cr17, IS 430, ISO X6Cr17, ISO 4016-430-00-I, JIS SUS430, GOST 12Ch17, KS STS430, UNS S43000, ASTM 430, AISI 430, DIN 1.4016, DIN X8Cr17, DIN X3CrTi17, AFNOR Z8C17, BS 430S15, UNI X8Cr17, SS 2320, UNE F.3113, SAE 430, JIS SUS430TP, JIS SUS430TB, JIS SUS430TKA, JIS SUS430TKC, JIS SUSY430, EN X6Cr17, EN 1.4016, ISO F1, GB 1Cr17, ASTM S43000
DIN 5512-3 Grade X6Cr17 soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 g/cm³ |
DIN 5512-3 Grade X6Cr17 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 25 W/(m·K) |
- |
DIN 5512-3 Grade X6Cr17 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 16 - 18 % |
| Manganese |
Manganese of 1 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
DIN 5512-3 Grade X6Cr17 soft annealed (+A) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
DIN 5512-3 Grade X6Cr17 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 220 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 215 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 195 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 8 - 20 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 18 - 20 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 18 - 20 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 18 - 20 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 400 - 950 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 430 - 630 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 200 - 320 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 220 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 215 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 210 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 200 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 195 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 190 - 196 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 260 - 280 MPa |
- |