JIS G4304 Grade SUS430 annealed
Equivalent material: GB/T 1Cr17, GB/T 1Cr17-Q, GB 1Cr17, GB 1Cr15, GOST 12Х17, GOST 12H17, AS 430, DIN X6Cr17, NF Z8C17, BS 430S15, BS 430S17, IS 05Cr17, IS 08Cr17, UNI X8Cr17, EN X6Cr17, UNE X8Cr17, UNE X6Cr17, UNE F.310.D, SIS 2320, AMS 5503, AMS 5627, ASME 430, ASTM TP430, ASTM 430, ASTM F430, ASTM MT430, ASTM WP430, MIL 430, JIS SUS430TB, AISI 430, SAE 430, GB/T ML1Cr17, GB Y1Cr17, AS 430F, DIN X12CrMoS17, NF Z10CF17, NF Z13CF17, UNI X10CrS17, UNE X10CrS17, SIS 2383-02, SIS 2383-03, SIS 2383, ASTM 430F, MIL 430F, JIS SUS430F, AISI 430F, UNS S43000, DIN 1.4016, DIN X8Cr17, DIN X3CrTi17, AFNOR Z8C17, SS 2320, UNE F.3113, JIS SUS430TP, JIS SUS430TKA, JIS SUS430TKC, JIS SUSY430, EN 1.4016, ISO X6Cr17, ISO F1, GOST 12Ch17, ASTM S43000
JIS G4304 Grade SUS430 annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS430 annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS430 annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS430 annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 88 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 450 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |