JIS G3457 Grade STPY400
Equivalent material: DIN 1.0253, DIN USt 37.0, JIS STPG370, EN 1.0253, DIN 1.0254, DIN St 37.0, AFNOR TU 37 B, AFNOR TU E 220 A, BS P235T1, BS S360, JIS 12A, EN P235T1, EN P235TR1, EN 1.0254, ASTM Grade A, AFNOR TS E 235 A, AFNOR TS E 24-a, AFNOR TS E 235, BS L235, BS ERW360, JIS STC370, EN L235, DIN 1.0255, DIN St 37-4, DIN St 37.4, AFNOR TU E 220, BS P235T2, JIS STS370, EN P235T2, EN P235TR2, EN 1.0255, AFNOR TS 37 CP, ASTM Grade Y 35
JIS G3457 Grade STPY400 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3457 Grade STPY400 thermal
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 15 - 18 % |
- |
| Elongation A5, transverse |
23.0 °C |
Elongation A5, transverse of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 400 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 225 MPa |
- |
JIS G3457 Grade STPY400 chemical
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3457 Grade STPY400 magnetic
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3457 Grade STPY400 electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3457 Grade STPY400 mechanical
| Property |
Value |
| Wall thickness |
Wall thickness of 5 - 8 mm |