JIS G3446 Grade SUS430TKC
Equivalent material: DIN 1.4016, DIN X6Cr17, DIN X8Cr17, DIN X3CrTi17, AFNOR Z8C17, BS 430S15, UNI X8Cr17, SS 2320, UNE F.3113, AISI 430, SAE 430, JIS SUS430, JIS SUS430TP, JIS SUS430TB, JIS SUS430TKA, JIS SUSY430, EN X6Cr17, EN 1.4016, ISO X6Cr17, ISO F1, GOST 12Ch17, GB 1Cr17, ASTM S43000, UNS S43000
JIS G3446 Grade SUS430TKC general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G3446 Grade SUS430TKC thermal
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 11 - 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 410 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 245 MPa |
- |
JIS G3446 Grade SUS430TKC magnetic
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G3446 Grade SUS430TKC electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G3446 Grade SUS430TKC mechanical
| Property |
Value |
| Wall thickness |
Wall thickness of 1 - 8 mm |