JIS G3202 Grade SFVC1
Equivalent material: DIN 1.0352, DIN P245GH, AFNOR P245GH, BS P245GH, EN P245GH, EN 1.0352, ASTM Grade WPL6, UNS K03006, UNS K03506
JIS G3202 Grade SFVC1 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3202 Grade SFVC1 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3202 Grade SFVC1 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3202 Grade SFVC1 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3202 Grade SFVC1 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 21 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 38 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 410 - 560 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 205 MPa |
- |