EN 10028-3 Grade P275N normalized or normalized formed (+N)
EN 10028-3 Grade P275N normalized or normalized formed (+N) introduction
Weldable fine grain steel (unalloyed quality steel) for application in steam boiler and pressure vessel construction.
Equivalent material: AFNOR E263+4, BS 224-400, ASTM Grade 6, DIN StE285, DIN 1.0486, DIN StE 285, JIS STK400, JIS SM400, JIS SM400A, JIS SM400C, JIS SM400B, EN StE285, EN 1.0486, ASTM Grade A, ASTM Grade WPL6
EN 10028-3 Grade P275N normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.84 - 7.85 g/cm³ |
EN 10028-3 Grade P275N normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 430 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 52.6 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 53.4 - 54 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 53.3 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 50.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 46.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 43.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 39.5 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 36.1 W/(m·K) |
- |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 18 mm²/s |
- |
| - |
20.0 °C |
Thermal diffusivity of 14.8 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 13.7 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.1 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
EN 10028-3 Grade P275N normalized or normalized formed (+N) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.18 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.5 - 1.4 % |
| Molybdenum |
Molybdenum of 0.08 % |
| Nickel |
Nickel of 0.5 % |
| Niobium |
Niobium of 0.05 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.025 % |
| Titanium |
Titanium of 0.03 % |
| Vanadium |
Vanadium of 0.05 % |
EN 10028-3 Grade P275N normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10028-3 Grade P275N normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 1.3E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 1.95E-7 - 2E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.4E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.15E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.03E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.26E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.68E-7 Ω·m |
EN 10028-3 Grade P275N normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 22 - 24 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 340 - 510 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 215 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 225 - 275 MPa |
- |