JIS G3128 Grade E355E
Equivalent material: DIN 1.0566, DIN TStE 355, DIN TStE355, DIN P355NL1, DIN A350LF2, AFNOR P355NL1, AFNOR A510FP1, AFNOR A510FP, BS 225-490 A, BS P355NL1, UNI A510 FP, JIS SLA37, JIS SLA365, JIS STK50, JIS STK51, JIS STK490, JIS STK500, EN P355NL1, EN 1.0566, ISO E355-E, ISO P355NL1, ISO PT490ML1, ISO PT490ML3, ISO PT490QL2, ISO E355E, GB/T L14204, GB/T Q420q-D, UNS K01600, UNS K02003, UNS K02007, UNS K02010, UNS K02302, UNS K02700, UNS K02701, UNS K02803, UNS K03301, UNS K11803, UNS K12037, UNS K12609
JIS G3128 Grade E355E general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3128 Grade E355E thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3128 Grade E355E magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3128 Grade E355E electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3128 Grade E355E mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Impact strength, Charpy notched |
-50.0 °C |
Impact strength, Charpy notched of 27 kJ/m² |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 430 - 630 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 285 - 355 MPa |
- |
| impactTransVNotch |
-50.0 °C |
impactTransVNotch of 16 kJ/m² |
- |