ISO 4957 Grade S12-1-4-5 quenched (+Q)
ISO 4957 Grade S12-1-4-5 quenched (+Q) introduction
High V-Co alloyed top high speed steel with highest wear resistance, high hot hardness and tempering resistance.
Application: face and scrub tools
Equivalent material: GB W12Cr4V5Co5, CSN 19858, BS BT15, ISO HS12-1-5-5, UNE F.5563, AISI T15, DIN 1.3202, DIN HS12-1-4-5, AFNOR Z160WKCV12-05-05-04, UNI HS12-1-5-5, UNE 12-1-5-5, SAE T15, JIS SKH10, EN 1.3202, GOST R13F4K5, GB/T T71245, GB/T W12Cr4V5Co5, ASTM Type T15, UNS T12015
ISO 4957 Grade S12-1-4-5 quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8.12 g/cm³ |
ISO 4957 Grade S12-1-4-5 quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 9.6E-6 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.16E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1425 °C |
Typical for Tool And Machining Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 460 J/(kg·K) |
Typical for Tool And Machining Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 27.6 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 27.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 27.7 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 27.5 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 27 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 26.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 26.1 W/(m·K) |
- |
ISO 4957 Grade S12-1-4-5 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 1.3 - 1.45 % |
| Chromium |
Chromium of 3.8 - 4.5 % |
| Cobalt |
Cobalt of 4.5 - 5 % |
| Manganese |
Manganese of 0.4 % |
| Molybdenum |
Molybdenum of 0.7 - 1 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.45 % |
| Sulfur |
Sulfur of 0.03 % |
| Tungsten |
Tungsten of 11.5 - 12.5 % |
| Vanadium |
Vanadium of 3.5 - 4 % |
ISO 4957 Grade S12-1-4-5 quenched (+Q) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 5.24E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 5.81E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 6.64E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 7.51E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 8.44E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 9.41E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.04E-6 Ω·m |
ISO 4957 Grade S12-1-4-5 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 224 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 220 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 214 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 191 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 180 GPa |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 79 GPa |
Typical for Tool And Machining Steel |