EN 10277-4 Grade 15NiCr13 treated to ferritic-pearlite structure and turned (+FP+SH)
EN 10277-4 Grade 15NiCr13 treated to ferritic-pearlite structure and turned (+FP+SH) introduction
As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: SAE (3311), UNS G33106, DIN 1.5752, DIN 14NiCr14, DIN 15NiCr13, AFNOR 12NC15, BS 655M13, AISI 3415, AISI 3310, SAE 3415, SAE 3310, JIS SNC815H, JIS SNC815HRCH, JIS SNC815RCH, JIS SNC815, EN 1.5752, ASTM E3310, ASTM Grade 3310RH
EN 10277-4 Grade 15NiCr13 treated to ferritic-pearlite structure and turned (+FP+SH) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-4 Grade 15NiCr13 treated to ferritic-pearlite structure and turned (+FP+SH) thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 44 W/(m·K) |
EN 10277-4 Grade 15NiCr13 treated to ferritic-pearlite structure and turned (+FP+SH) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Chromium |
Chromium of 0.6 - 0.9 % |
| Manganese |
Manganese of 0.4 - 0.7 % |
| Nickel |
Nickel of 3 - 3.5 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10277-4 Grade 15NiCr13 treated to ferritic-pearlite structure and turned (+FP+SH) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 166 - 217 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
Our stringent quality control measures guarantee the highest standards of steel.
-- Our promise
Similar or equivalent steel materials