EN 10084 Grade 15NiCr13 quenched (+Q)
EN 10084 Grade 15NiCr13 quenched (+Q) introduction
The steel 15NiCr13 is used particularly for high loaded gear parts (gear wheels, pinions, pins), but also in the mechanical engineering.
Equivalent material: EN 1.5752, IS 13Ni13Cr3, ISO 15NiCr13, JIS SNC815, JIS SNC815H, KS SNC815H, ASTM A506 Grade E3310, ASTM A837 Grade E3310, ASTM A914 Grade 3310RH, SAE 3310, UNS G33106, DIN 14NiCr14, DIN 1.5752, DIN 15NiCr13, AFNOR 12NC15, BS 655M13, AISI 3415, AISI 3310, SAE 3415, JIS SNC815HRCH, JIS SNC815RCH, ASTM E3310, ASTM Grade 3310RH
EN 10084 Grade 15NiCr13 quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10084 Grade 15NiCr13 quenched (+Q) thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 44 W/(m·K) |
EN 10084 Grade 15NiCr13 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Chromium |
Chromium of 0.6 - 0.9 % |
| Copper |
Copper of 0.4 % |
| Manganese |
Manganese of 0.4 - 0.7 % |
| Nickel |
Nickel of 3 - 3.5 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10084 Grade 15NiCr13 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 700 - 1000 MPa |
- |